制备方法如下：（J. Phys. Chem. B 2001, 105, 4065-4067）
Preparation of 3.5 nm Seed. A 20 mL aqueous solution containing 2.5X10-4 M HAuCl4 and 2.5X10-4 M tri-sodium citrate was prepared in a conical flask. Next, 0.6 mL of ice cold
0.1 M NaBH4 solution was added to the solution all at once while stirring. The solution turned pink immediately after adding NaBH4, indicating particle formation. The particles in this solution were used as seeds within 2-5 h after preparation.
问题1：合成步骤中的2.5X10-4 M是这20 mL体系中每种物质的物质的量还是它们在这个体系中的浓度？
问题2：该反应还原剂的量是如何确定的？为何需要冰冷？
问题3：很多文献在颜色变化中提到酒红色，但是我个人感觉酒红色跟粉色差别还是比较大的，3.5 nm的尺寸，该是什么颜色的呢？
问题4：合成过程结束到2-5小时之间都是一个熟化过程么？在这个过程中晶粒会长大多少？在什么样的条件下进行熟化更为合适？
谢谢大家，希望得到大家的指点！

制备方法如下：（J. Phys. Chem. B 2001, 105, 4065-4067）
Preparation of 3.5 nm Seed. A 20 mL aqueous solution containing 2.5X10-4 M HAuCl4 and 2.5X10-4 M tri-sodium citrate was prepared in a conical flask. Next, 0.6 mL of ice cold
0.1 M NaBH4 solution was added to the solution all at once while stirring. The solution turned pink immediately after adding NaBH4, indicating particle formation. The particles in this solution were used as seeds within 2-5 h after preparation.
问题1：合成步骤中的2.5X10-4 M是这20 mL体系中每种物质的物质的量还是它们在这个体系中的浓度？
问题2：该反应还原剂的量是如何确定的？为何需要冰冷？
问题3：很多文献在颜色变化中提到酒红色，但是我个人感觉酒红色跟粉色差别还是比较大的，3.5 nm的尺寸，该是什么颜色的呢？
问题4：合成过程结束到2-5小时之间都是一个熟化过程么？在这个过程中晶粒会长大多少？在什么样的条件下进行熟化更为合适？
谢谢大家，希望得到大家的指点！

1.M是浓度单位，当然是指浓度。
2.还原剂的量应该是经过实验摸索出来的。NaBH4在冰冷条件下才稳定，要不然会分解。
3.可以自己试试，看长出来是什么颜色。
4.应该是在这段时间内在成核生长，到3.5nm就稳定了。条件的话一般是室温吧，文章中或许有提到。

一般3.5nm的AU种是淡黄色的~ 一般Au纳米的熟化都是4度冰箱里，保存也是这个条件。

1、2两个问题2楼说的挺对的，
3个个人觉得做的不一定是粉红色，这只是SEEDS，如果长成金particles后就不会是了。
第四个在这个时间里应该是一个敦化过程

刚还原的金纳米粒子还不是特别稳定，有些晶核还会继续成长，还有一种说法是金纳米粒子的自催化作用

那HAuCl4和NaBH4的质量好少啊，这种情况下怎么实现称量呢？谢谢各位

先配一定量浓度较高的个溶液 然后稀释不就行了

我现在正在做小颗粒的金纳米粒子，我用的方法和你上述一模一样，我觉得0.6ml的NaBH4（0.1M）加的太多了，我做出来的颜色是青绿色……可以请教一下你的配比吗？