现在做的是镁合金中长周期堆垛结构，对试样做了TEM，但是衍射斑点为啥是这样，并不像文献中那样子，现在也不知道怎么标定。麻烦哪位老师给看看

下图细条纹的衍射斑点
对应斑点的值

截屏太差了，重新做一张吧。

现在想问一下牛人，没有出现想要的衍射斑点原因是什么？
1）选区没有选好
2）照的时候没有调整好角度，还是没有选好入射方向。
3）第一张图片中的层片不是长周期结构
还是有什么问题···

您说的是第一张吗，这个对衍射斑点没有影响吧

为什么我们做不出来人这张效果

偶说的是沙发，看着太乱。

The long-period stacking order (LPSO) structures in rapidly solidified Mg97Zn1Y2 alloy have been studied by conventional and highresolution
transmission electron microscopes (HRTEMs). There are four kinds of stacking sequences in the LPSO structures, i.e., 18R of
ABABABCACACABCBCBC, 14H ofACBCBABABABCBC, 10H ofABACBCBCABand 24R ofABABABABCACACACABCBCBCBC.
The 18R structure is dominantly observed in the present study. The rest three are occasionally observed in places. The 10H and 24R structures
are recently discovered. The lattice constants of 18R(1 -1 1 -1 2)3, 14H(-2 1 -2 1 -1 1 -1 2-1 2), 10H(1 -3 1 -1 3 -1) and 24R(1 -1 1 -1 1 -1 2)3 structures are
estimated to be a = 0.320 nm and c = 4.678 nm, a = 0.325 nm and c = 3.694 nm, a = 0.325 nm and c = 2.603 nm, a = 0.322 nm and c = 6.181 nm
for the hexagonal structure, respectively
不知道在我这张图中怎么去标a，c的值

这位同学，贴图的目的是为了别人看起来更清晰方便，更容易帮助你解决问题，对吧？你第一次贴图格式乱了，请你重新做一张。现在这张格式依然有问题，数据和栏目位置依然错乱，而且字体小得看不清楚。你没有试试自己看这张图片会得到什么有用的信息？如果自己看着有困难，是不是别人看起来会更困难？

老师说的是，已改过．．．．．．．